29673175-3	2018	The grain size of the obtained alpha copper phase was around 5 μm. The best properties were achieved at 220 J/mm2 laser energy density with a density of 8.82 g/cm3, hardness of 78.2 HRB (Rockwell Hardness measured on the B scale), yield strength of 399 MPa, tensile strength of 490 MPa, and an elongation that reached 19%.	Copper	37-43	ArfGAP with FG repeats 1	Homo sapiens	189-192