30866174-4	2019	In electrochemical testing, the trimetallic oxide CoFeNi-O-1 (derived from the MOG with a Co/Fe/Ni molar ratio of 5:1:4) exhibits remarkable catalytic activity with a low overpotential of 244 mV at a current density of 10 mA cm-2 and a small Tafel slope of 55.4 mV dec-1 in alkaline electrolyte, outperforming most recently reported electrocatalysts.	Cobalt	50-52	deleted in esophageal cancer 1	Homo sapiens	265-270	
31887727-3	2020	Because of the variation of phase and morphology, only 448 mV can deliver a current density of 10 mA cm-2 with a small Tafel slope (61 mV dec-1) for mesoporous cobalt tungsten oxide hydroxide, while the cobalt tungstate nanoparticles can not satisfy the basic demand of electrocatalysts.	Cobalt	160-166	deleted in esophageal cancer 1	Homo sapiens	138-143	
30191682-6	2018	The Tafel slopes of the Fe, Co, Ni, Cu, and Ag disks in 1 m KOH+Fe3+ electrolyte were in the range of 29-42 mV dec-1 .	Cobalt	28-30	deleted in esophageal cancer 1	Homo sapiens	111-116	
30470747-3	2018	Impressively, the cobalt-substituted ruthenium nanosheets only need an extremely low overpotential of 13 mV to achieve a current density of 10 mA cm-2 in 1 M KOH media and an ultralow Tafel slope of 29 mV dec-1, which exhibit top-level catalytic activity among all reported platinum-free electrocatalysts.	Cobalt	18-24	deleted in esophageal cancer 1	Homo sapiens	205-210	
26671419-3	2016	The experimental results indicated that the HER activity of C@Ni2-x Cox P catalyst is strongly related to the Co/Ni ratio, and the C@NiCoP got the highest HER activity with low onset potential of ~45 mV, small Tafel slope of ~43 mV dec(-1) , large exchange current density of 0.21 mA cm(-2) , and high long-term durability (60 h) in 0.5 m H2 SO4 solutions.	Cobalt	68-70	deleted in esophageal cancer 1	Homo sapiens	232-238	
30230234-4	2018	With a trace cobalt loading (0.46 wt%), the electrodes achieve a low Tafel slope of 46 mV dec-1 and overpotential of only 69 mV at a current density of 10 mA cm-2 in 0.5 m H2 SO4 .	Cobalt	13-19	deleted in esophageal cancer 1	Homo sapiens	90-95	
29624891-7	2018	The Tafel slope of Co@N-Carbon was 61 mV dec-1 , which is comparable to that of commercial RuO2 (58 mV dec-1 ).	Cobalt	19-21	deleted in esophageal cancer 1	Homo sapiens	41-46	
29624891-7	2018	The Tafel slope of Co@N-Carbon was 61 mV dec-1 , which is comparable to that of commercial RuO2 (58 mV dec-1 ).	Cobalt	19-21	deleted in esophageal cancer 1	Homo sapiens	103-108