32028687-4	2020	For oil containing 0.1 wt% graphene at a rotational speed of 3000 r min-1 and 40 N loads, the average friction coefficient was reduced by 76.33%.	Graphite	27-35	CD59 molecule (CD59 blood group)	Homo sapiens	68-73	
32028687-6	2020	For oil containing 0.05 wt% graphene at a lower rotational speed of 500 r min-1 and a higher load of 140 N, the temperature rise was reduced by 19.76%.	Graphite	28-36	CD59 molecule (CD59 blood group)	Homo sapiens	74-79	
29378400-3	2018	By precisely controlling their parts per million level concentrations, centimeter-sized single-crystal graphene is obtained in a reliable manner with a maximum growth rate up to 190 mum min-1.	Graphite	103-111	CD59 molecule (CD59 blood group)	Homo sapiens	186-191	
31858035-2	2019	This method realizes rapid and controllable fabrication of uniform graphene microspheres with up to 800 muL min-1 (ca.	Graphite	67-75	CD59 molecule (CD59 blood group)	Homo sapiens	108-113	
29802330-6	2018	The highest degradation rate was found to be 9.66 x 10-6 min-1, achieved by the sample grown at 700  C for 5 min, which was 62% higher than the sample just treated at that temperature without graphene growth.	Graphite	192-200	CD59 molecule (CD59 blood group)	Homo sapiens	57-62	
31430126-4	2019	The highly enhanced domain growth rate (~37 nm min-1) and the quick nucleation rate (~1200 nuclei min-1 cm-2) both account for this high productivity of graphene film.	Graphite	153-161	CD59 molecule (CD59 blood group)	Homo sapiens	47-52	
31430126-4	2019	The highly enhanced domain growth rate (~37 nm min-1) and the quick nucleation rate (~1200 nuclei min-1 cm-2) both account for this high productivity of graphene film.	Graphite	153-161	CD59 molecule (CD59 blood group)	Homo sapiens	98-103	
29125685-4	2018	Ethane condition gives a growth rate about four times faster than methane, achieving about 420 microm min-1 for the growth of sub-centimeter graphene single crystals at temperature about 1000  C. In addition, the temperature threshold to obtain graphene using ethane can be reduced to 750  C, lower than the general growth temperature threshold (about 1000  C) with methane on copper foil.	Graphite	141-149	CD59 molecule (CD59 blood group)	Homo sapiens	102-107	
29125685-4	2018	Ethane condition gives a growth rate about four times faster than methane, achieving about 420 microm min-1 for the growth of sub-centimeter graphene single crystals at temperature about 1000  C. In addition, the temperature threshold to obtain graphene using ethane can be reduced to 750  C, lower than the general growth temperature threshold (about 1000  C) with methane on copper foil.	Graphite	245-253	CD59 molecule (CD59 blood group)	Homo sapiens	102-107	
28501570-3	2017	The apparent rate constant of levofloxacin decay was found to be 0.2883 min-1 for graphite felt-10 with the best performance at 200 mA, which is lower than graphite felt at 400 mA.	Graphite	82-90	CD59 molecule (CD59 blood group)	Homo sapiens	72-77	
27562642-2	2016	The maximum growth rate can reach 300 mum min-1 , several orders of magnitude higher than previously reported values for millimeter-sized single-crystalline graphene growth on Cu foils.	Graphite	157-165	CD59 molecule (CD59 blood group)	Homo sapiens	42-47	
27589373-8	2016	The asymmetric charge coated microporous activated graphene exhibits exceptional electrosorption capacity of 18.43 mg g(-1) at a flow rate of 20 mL min(-1) upon applied cell potential of 1.4 V with initial NaCl concentration of 300 mg L(-1), high charge efficiency, excellent recyclability, and, moreover, good antibacterial behavior.	Graphite	51-59	CD59 molecule (CD59 blood group)	Homo sapiens	148-154	
28665430-4	2017	Our strategy allowed the successful preparation of sub-centimeter-domain-sized graphene in 1 h with an average growth rate of 70 mum min-1, and with a hole mobility of 5500 cm2 V-1 S-1, which is sufficient for practical applications.	Graphite	79-87	CD59 molecule (CD59 blood group)	Homo sapiens	133-138	
27061704-1	2016	A second passivation and a multistage carbon-source supply (CSS) allow a 50-fold enhancement of the growth rate of large single-crystalline graphene with a record growth rate of 101 mum min(-1) , almost 10 times higher than for pure copper.	Graphite	140-148	CD59 molecule (CD59 blood group)	Homo sapiens	186-192	
25024132-6	2014	Both Ag/CNT-CHI/graphite immunoelectrodes (using MAGE A2 and MAGE A11) were independently capable of distinguishing specific and nonspecific analytes like CD59, D-dimers, etc.	Graphite	16-24	CD59 molecule (CD59 blood group)	Homo sapiens	155-159